| Non. | Pwopriyete rezin | Valè tipik | Inite | Metòd Tès la |
| 1 | Gravite espesifik, 23 ℃ | 1.05 | g/cm³ | ASTM D792 |
| 2 | Kontraksyon mwazi, 23 ℃, 3.2mm, 23 ℃ | 0.4-0.7 | % | ASTM D955 |
| 3 | To koule fonn, 220 ℃, 10 kg | 22 | g/10min | ASTM D1238 |
| 4 | Fòs tansyon nan sede, 23 ℃, 50mm/min, 3.2mm | 49 | MPa | ASTM D638 |
| 5 | Elongasyon tansyon nan sede, 23 ℃, 50 mm / min, 3.2 mm | 5 | %, (Minimòm) | ASTM D638 |
| 6 | Elongasyon tansyon nan kraze, 23'℃, 50mm/min, 3.2mm | 10 | %, (Minimòm) | ASTM D638 |
| 7 | Modil tansyon, 23 ℃, 50mm/min, 3.2mm | 2350 | MPa | ASTM D638 |
| 8 | Fòs fleksyon, 23 ℃, 15mm/min, 3.2mm | 78 | MPa | ASTM D790 |
| 9 | Modil fleksibilite, 23 ℃, 15 mm/min, 3.2 mm | 2550 | MPa | ASTM D790 |
| 10 | Fòs enpak Izod, ak dan, 3.2mm, 23℃ | 220 | J/m | ASTM D256 |
| 11 | Fòs enpak Izod, ak dan, 3.2mm, -30℃ | 90 | J/m | ASTM D256 |
| 12 | Fòs enpak Izod, ak dan, 6.4mm, 23℃ | 220 | J/m | ASTM D256 |
| 13 | Fòs enpak Izod, ak dan, 6.4mm, -30℃ | 90 | J/m | ASTM D256 |
| 14 | Dite Rockwell, Echèl R | 110 | / | ASTM D785 |
| 15 | HDT, sou kwen, 1.82MPa, 6.4mm, san rkui | 85 | °C | ASTM D648 |
| 16 | VICAT, 50N, 50℃/èdtan | 92 | °C | ASTM D1525 |
| 17 | RTI Elektrik | 95 | °C | UL 746B |
| 18 | RTI Mekanik ak Enpak | 95 | °C | UL 746B |
| 19 | RTI Mekanik san Enpak | 95 | °C | UL 746B |
| 20 | Enflamabilite, 1.5mm | HB | / | UL 94 |
| 21 | Enflamabilite, 3.0mm | HB | / | UL 94 |