HTA 108 se yon fim HDPE omopolimè ki fèt pou amelyore rèd ak baryè nan ko-ekstrizyon oswa nan melanj PE. Lè yo melanje l avèk LLDPE oswa metalosèn LLDPE, HTA 108 amelyore kapasite pwosesis yo.
Aplikasyon yo
Fim Soufle, Sak Pen, Retresi Koleksyon, Anbalaj Manje, Ranpli Fòm ak Sele Anbalaj, Ranpli Frizè...
Pwopriyete rezin
Valè tipik (Angle)
Valè Tipik (SI)
Tès ki baze sou
Dansite
0.961 g/cm³
0.961 g/cm³
A5TMD1505
Endis Fizyon2 (190*C/2.16 kg)
0.70 g/10 minit
0.70 g/10 minit
ASTM D1238
Endèks fonn chaj segondè (190 ℃ / 21.6 kg)
46 g/10 minit
46 g/10 minit
ASTM D1238
Pwopriyete fim
Valè tipik (Angle)
Valè Tipik (SI)
Tès ki baze sou
Fòs tansyon nan repo MD
8700 psi
60 MPa
ASTM D882
Fòs tansyon nan kraze TD
4500 psi
31 MPa
ASTM D882
Elongasyon nan Kraze MD
510%
510%
ASTM D882
Elongasyon nan Kraze TD
2%
2%
ASTM D882
Modil Sekant MD - 1% Sekant
17000 psi
1200 MPa
ASTM D882
Modil Sekant TD - 1% Sekant
25000 psi
1700 MPa
ASTM D882
Enpak lage flèch
<30g
<30g
ASTM D1709A
Elmendorf Chire Strength MD
10g
10g
ASTM D1922
Elmendorf Chire Strength TD
200g
200g
ASTM D1922
Deklarasyon Legal
Kontakte Reprezantan Sèvis Kliyan ExxonMobil Chemical ou a pou konfòmite potansyèl aplikasyon pou kontak ak manje (pa egzanp FDA, EL, HPFB).
Pwodui sa a pa fèt pou itilize nan aplikasyon medikal epi li pa ta dwe itilize nan okenn aplikasyon konsa.
Deklarasyon Processina
Yo te prepare echantiyon tès yo pou Pwen Ramolisman Vicat la lè l sèvi avèk ASTM D 4703. Yo te mezire tout pwopriyete ranpli yo sou ranpli ki gen yon epesè 25 pm (0.98 mil) (BUR 2.5: 1, extrusion pòch a 200 ℃ / 392'F). Ou ka jwenn pwopriyete fim ak melanj ko-extrudé yo nan Fèy Enfòmasyon HTA108 la.
Nòt
Pwopriyete tipik sa yo pa dwe entèprete kòm espesifikasyon. 1 Pwodwi a ka pa disponib nan youn oubyen plizyè peyi nan rejyon disponiblite yo idantifye yo. Tanpri kontakte reprezantan lavant ou pou jwenn tout disponiblite nan chak peyi.